MALDI-TOF characterisation of thermally generated gel from Nylon 66.

Saved in:
Bibliographic Details
Title: MALDI-TOF characterisation of thermally generated gel from Nylon 66.
Authors: Puglisi, Concetto1, Samperi, Filippo1, Di Giorgi, Sabrina2, Montaudo, Giorgio2 gmontaudo@dipchi.unict.it
Source: Polymer Degradation & Stability. Nov2002, Vol. 78 Issue 2, p369-378. 10p.
Abstract: Progress in understanding the thermal decomposition processes occurring in Nylon 66 (Ny66) was obtained by using matrix assisted laser desorption ionization-time of flight (MALDI-TOF) mass spectrometry techniques. Ny66 samples were subjected to thermal degradation under inert atmosphere heating them at 290 and 315 °C. The formation of a gel fraction was observed after about 15 min of heating and the addition of a condensing agent such as triphenyl phosphite (TPP) made the gelation complete in a few minutes. The MALDI-TOF mass spectra of the soluble fraction showed that secondary amino groups and cyclopentanone chain ends were generated in the heating process. The gel fraction was partially hydrolysed to destroy the network structure and the soluble material was analysed by MALDI-TOF. The spectra revealed the presence of N,N-substituted amide as side chains generated by the condensation of carboxyl end groups with secondary amino groups and azomethine structures originating from the reaction of cyclopentanone moieties with the terminal amino groups. These structures were most likely responsible for the gel formation on heating Ny66 samples. Comparison with similar experiments conducted on Ny6, showed that only secondary amino groups were formed in Ny6, leading to branched structures but not to crosslinking. [ABSTRACT FROM AUTHOR]
Copyright of Polymer Degradation & Stability is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
FullText Text:
  Availability: 0
Header DbId: egs
DbLabel: Engineering Source
An: 123015651
AccessLevel: 6
PubType: Academic Journal
PubTypeId: academicJournal
PreciseRelevancyScore: 0
IllustrationInfo
Items – Name: Title
  Label: Title
  Group: Ti
  Data: MALDI-TOF characterisation of thermally generated gel from Nylon 66.
– Name: Author
  Label: Authors
  Group: Au
  Data: <searchLink fieldCode="AR" term="%22Puglisi%2C+Concetto%22">Puglisi, Concetto</searchLink><relatesTo>1</relatesTo><br /><searchLink fieldCode="AR" term="%22Samperi%2C+Filippo%22">Samperi, Filippo</searchLink><relatesTo>1</relatesTo><br /><searchLink fieldCode="AR" term="%22Di+Giorgi%2C+Sabrina%22">Di Giorgi, Sabrina</searchLink><relatesTo>2</relatesTo><br /><searchLink fieldCode="AR" term="%22Montaudo%2C+Giorgio%22">Montaudo, Giorgio</searchLink><relatesTo>2</relatesTo><i> gmontaudo@dipchi.unict.it</i>
– Name: TitleSource
  Label: Source
  Group: Src
  Data: <searchLink fieldCode="JN" term="%22Polymer+Degradation+%26+Stability%22">Polymer Degradation & Stability</searchLink>. Nov2002, Vol. 78 Issue 2, p369-378. 10p.
– Name: Abstract
  Label: Abstract
  Group: Ab
  Data: Progress in understanding the thermal decomposition processes occurring in Nylon 66 (Ny66) was obtained by using matrix assisted laser desorption ionization-time of flight (MALDI-TOF) mass spectrometry techniques. Ny66 samples were subjected to thermal degradation under inert atmosphere heating them at 290 and 315 °C. The formation of a gel fraction was observed after about 15 min of heating and the addition of a condensing agent such as triphenyl phosphite (TPP) made the gelation complete in a few minutes. The MALDI-TOF mass spectra of the soluble fraction showed that secondary amino groups and cyclopentanone chain ends were generated in the heating process. The gel fraction was partially hydrolysed to destroy the network structure and the soluble material was analysed by MALDI-TOF. The spectra revealed the presence of N,N-substituted amide as side chains generated by the condensation of carboxyl end groups with secondary amino groups and azomethine structures originating from the reaction of cyclopentanone moieties with the terminal amino groups. These structures were most likely responsible for the gel formation on heating Ny66 samples. Comparison with similar experiments conducted on Ny6, showed that only secondary amino groups were formed in Ny6, leading to branched structures but not to crosslinking. [ABSTRACT FROM AUTHOR]
– Name: AbstractSuppliedCopyright
  Label:
  Group: Ab
  Data: <i>Copyright of Polymer Degradation & Stability is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract.</i> (Copyright applies to all Abstracts.)
PLink https://search.ebscohost.com/login.aspx?direct=true&site=eds-live&db=egs&AN=123015651
RecordInfo BibRecord:
  BibEntity:
    Identifiers:
      – Type: doi
        Value: 10.1016/S0141-3910(02)00188-X
    Languages:
      – Code: eng
        Text: English
    PhysicalDescription:
      Pagination:
        PageCount: 10
        StartPage: 369
    Titles:
      – TitleFull: MALDI-TOF characterisation of thermally generated gel from Nylon 66.
        Type: main
  BibRelationships:
    HasContributorRelationships:
      – PersonEntity:
          Name:
            NameFull: Puglisi, Concetto
      – PersonEntity:
          Name:
            NameFull: Samperi, Filippo
      – PersonEntity:
          Name:
            NameFull: Di Giorgi, Sabrina
      – PersonEntity:
          Name:
            NameFull: Montaudo, Giorgio
    IsPartOfRelationships:
      – BibEntity:
          Dates:
            – D: 01
              M: 11
              Text: Nov2002
              Type: published
              Y: 2002
          Identifiers:
            – Type: issn-print
              Value: 01413910
          Numbering:
            – Type: volume
              Value: 78
            – Type: issue
              Value: 2
          Titles:
            – TitleFull: Polymer Degradation & Stability
              Type: main
ResultId 1