Controllable synthesis of phenolic resin-based carbon aerogel templated by graphene oxide for high-performance supercapacitors.

Saved in:
Bibliographic Details
Title: Controllable synthesis of phenolic resin-based carbon aerogel templated by graphene oxide for high-performance supercapacitors.
Authors: Chang, Meng-Jie1,2 (AUTHOR) mengjie_chang@xust.edu.cn, Zhu, Wen-Yao1 (AUTHOR), Ni, Fu-Rong1 (AUTHOR), Wang, Hui1 (AUTHOR), Li, Xin1 (AUTHOR), Yang, Liu-Qing2 (AUTHOR), Li, Hui-Lu1 (AUTHOR), Liu, Jun1 (AUTHOR)
Source: Colloids & Surfaces A: Physicochemical & Engineering Aspects. Jan2024, Vol. 681, pN.PAG-N.PAG. 1p.
Subjects: Graphene oxide, Aerogels, Supercapacitors, Scanning electron microscopy, Carbon
Abstract: In this work, porous phenol formaldehyde carbon aerogel (PFCA) was facilely manufactured by using simple hydrothermal method and ambient pressure drying. The micromorphology, specific area and electrochemical characteristic of the produced carbon aerogel were examined with scanning electron microscopy, nitrogen adsorption-desorption tests, cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance spectroscopy. The effects of catalyst and phenol addition, and solvent type on the structure and property have been systematically studied. The results show that the PFCA has a three-dimensional "bead chain" network structure and the typical PFCA-7.5/8 sample exhibits high specific surface area of 759.02 m2 g−1. Moreover, the graphene oxide composited phenol formaldehyde carbon aerogel (GO/PFCA) presenting a lamellar structure was developed by using GO as template. The optimum PFCA-7.5/8 prepared with ethanol as solvent has the best electrochemical performance of 138.33 F g−1 at 5 mV s−1 in 6 M KOH electrolyte, which can be improved to 150.00 F g−1 for the GO/PFCA-3 sample. [Display omitted] [ABSTRACT FROM AUTHOR]
Copyright of Colloids & Surfaces A: Physicochemical & Engineering Aspects is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Description
Abstract:In this work, porous phenol formaldehyde carbon aerogel (PFCA) was facilely manufactured by using simple hydrothermal method and ambient pressure drying. The micromorphology, specific area and electrochemical characteristic of the produced carbon aerogel were examined with scanning electron microscopy, nitrogen adsorption-desorption tests, cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance spectroscopy. The effects of catalyst and phenol addition, and solvent type on the structure and property have been systematically studied. The results show that the PFCA has a three-dimensional "bead chain" network structure and the typical PFCA-7.5/8 sample exhibits high specific surface area of 759.02 m2 g−1. Moreover, the graphene oxide composited phenol formaldehyde carbon aerogel (GO/PFCA) presenting a lamellar structure was developed by using GO as template. The optimum PFCA-7.5/8 prepared with ethanol as solvent has the best electrochemical performance of 138.33 F g−1 at 5 mV s−1 in 6 M KOH electrolyte, which can be improved to 150.00 F g−1 for the GO/PFCA-3 sample. [Display omitted] [ABSTRACT FROM AUTHOR]