Benchmark of J55 and X56 steels on cracking and corrosion effects under hydrogen salt cavern boundary conditions.

Saved in:
Bibliographic Details
Title: Benchmark of J55 and X56 steels on cracking and corrosion effects under hydrogen salt cavern boundary conditions.
Authors: Janßen, Holger1,2 (AUTHOR) holger.janssen@dlr.de, Ehmcke, Luisa1,3 (AUTHOR), Satola, Barbara1 (AUTHOR), Kroener, Michael1 (AUTHOR), Dyck, Alexander1 (AUTHOR), Vehse, Martin1 (AUTHOR), Wark, Michael2 (AUTHOR), Agert, Carsten1,4 (AUTHOR)
Source: International Journal of Hydrogen Energy. Mar2024, Vol. 60, p1392-1403. 12p.
Subjects: Stress corrosion cracking, Energy dispersive X-ray spectroscopy, Caves, Hydrogen as fuel, Surface cracks
Abstract: Salt caverns have great potential to store relevant amounts of hydrogen as part of the energy transition. However, the durability and suitability of commonly used steels for piping in hydrogen salt caverns is still under research. In this work, aging effects focusing on corrosion and cracking patterns of casing steel API 5CT J55 and "H2ready" pipeline steel API 5L X56 were investigated with scanning electron microscopy and energy dispersive X-ray spectroscopy after accelerated stress tests with pressure/temperature cycling under hydrogen salt cavern-like conditions. Compared to dry conditions, significant more corrosion by presence of salt ions was detected. However, compared to X56, only for J55 an intensification of corrosion and cracking at the surface due to hydrogen atmosphere was revealed. Pronounced surface cracks were observed for J55 over the entire samples. Overall, the results strongly suggest that X56 is more resistant than J55 under the conditions of a hydrogen salt cavern. • Investigation of casing steel API 5CT J55 and "H2ready" pipeline steel API 5L X56. • Determination of aging effects under hydrogen salt cavern boundary conditions. • For J55, intensification of surface corrosion due to H 2 atmosphere was detected. • Pronounced surface cracks were observed only for J55 over the entire samples. • Results show that X56 is more resistant than J55 to H 2 salt cavern conditions. [ABSTRACT FROM AUTHOR]
Copyright of International Journal of Hydrogen Energy is the property of Pergamon Press - An Imprint of Elsevier Science and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
FullText Text:
  Availability: 0
Header DbId: egs
DbLabel: Engineering Source
An: 175939060
AccessLevel: 6
PubType: Academic Journal
PubTypeId: academicJournal
PreciseRelevancyScore: 0
IllustrationInfo
Items – Name: Title
  Label: Title
  Group: Ti
  Data: Benchmark of J55 and X56 steels on cracking and corrosion effects under hydrogen salt cavern boundary conditions.
– Name: Author
  Label: Authors
  Group: Au
  Data: <searchLink fieldCode="AR" term="%22Janßen%2C+Holger%22">Janßen, Holger</searchLink><relatesTo>1,2</relatesTo> (AUTHOR)<i> holger.janssen@dlr.de</i><br /><searchLink fieldCode="AR" term="%22Ehmcke%2C+Luisa%22">Ehmcke, Luisa</searchLink><relatesTo>1,3</relatesTo> (AUTHOR)<br /><searchLink fieldCode="AR" term="%22Satola%2C+Barbara%22">Satola, Barbara</searchLink><relatesTo>1</relatesTo> (AUTHOR)<br /><searchLink fieldCode="AR" term="%22Kroener%2C+Michael%22">Kroener, Michael</searchLink><relatesTo>1</relatesTo> (AUTHOR)<br /><searchLink fieldCode="AR" term="%22Dyck%2C+Alexander%22">Dyck, Alexander</searchLink><relatesTo>1</relatesTo> (AUTHOR)<br /><searchLink fieldCode="AR" term="%22Vehse%2C+Martin%22">Vehse, Martin</searchLink><relatesTo>1</relatesTo> (AUTHOR)<br /><searchLink fieldCode="AR" term="%22Wark%2C+Michael%22">Wark, Michael</searchLink><relatesTo>2</relatesTo> (AUTHOR)<br /><searchLink fieldCode="AR" term="%22Agert%2C+Carsten%22">Agert, Carsten</searchLink><relatesTo>1,4</relatesTo> (AUTHOR)
– Name: TitleSource
  Label: Source
  Group: Src
  Data: <searchLink fieldCode="JN" term="%22International+Journal+of+Hydrogen+Energy%22">International Journal of Hydrogen Energy</searchLink>. Mar2024, Vol. 60, p1392-1403. 12p.
– Name: Subject
  Label: Subjects
  Group: Su
  Data: <searchLink fieldCode="DE" term="%22Stress+corrosion+cracking%22">Stress corrosion cracking</searchLink><br /><searchLink fieldCode="DE" term="%22Energy+dispersive+X-ray+spectroscopy%22">Energy dispersive X-ray spectroscopy</searchLink><br /><searchLink fieldCode="DE" term="%22Caves%22">Caves</searchLink><br /><searchLink fieldCode="DE" term="%22Hydrogen+as+fuel%22">Hydrogen as fuel</searchLink><br /><searchLink fieldCode="DE" term="%22Surface+cracks%22">Surface cracks</searchLink>
– Name: Abstract
  Label: Abstract
  Group: Ab
  Data: Salt caverns have great potential to store relevant amounts of hydrogen as part of the energy transition. However, the durability and suitability of commonly used steels for piping in hydrogen salt caverns is still under research. In this work, aging effects focusing on corrosion and cracking patterns of casing steel API 5CT J55 and "H2ready" pipeline steel API 5L X56 were investigated with scanning electron microscopy and energy dispersive X-ray spectroscopy after accelerated stress tests with pressure/temperature cycling under hydrogen salt cavern-like conditions. Compared to dry conditions, significant more corrosion by presence of salt ions was detected. However, compared to X56, only for J55 an intensification of corrosion and cracking at the surface due to hydrogen atmosphere was revealed. Pronounced surface cracks were observed for J55 over the entire samples. Overall, the results strongly suggest that X56 is more resistant than J55 under the conditions of a hydrogen salt cavern. • Investigation of casing steel API 5CT J55 and "H2ready" pipeline steel API 5L X56. • Determination of aging effects under hydrogen salt cavern boundary conditions. • For J55, intensification of surface corrosion due to H 2 atmosphere was detected. • Pronounced surface cracks were observed only for J55 over the entire samples. • Results show that X56 is more resistant than J55 to H 2 salt cavern conditions. [ABSTRACT FROM AUTHOR]
– Name: AbstractSuppliedCopyright
  Label:
  Group: Ab
  Data: <i>Copyright of International Journal of Hydrogen Energy is the property of Pergamon Press - An Imprint of Elsevier Science and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract.</i> (Copyright applies to all Abstracts.)
PLink https://search.ebscohost.com/login.aspx?direct=true&site=eds-live&db=egs&AN=175939060
RecordInfo BibRecord:
  BibEntity:
    Identifiers:
      – Type: doi
        Value: 10.1016/j.ijhydene.2024.02.168
    Languages:
      – Code: eng
        Text: English
    PhysicalDescription:
      Pagination:
        PageCount: 12
        StartPage: 1392
    Subjects:
      – SubjectFull: Stress corrosion cracking
        Type: general
      – SubjectFull: Energy dispersive X-ray spectroscopy
        Type: general
      – SubjectFull: Caves
        Type: general
      – SubjectFull: Hydrogen as fuel
        Type: general
      – SubjectFull: Surface cracks
        Type: general
    Titles:
      – TitleFull: Benchmark of J55 and X56 steels on cracking and corrosion effects under hydrogen salt cavern boundary conditions.
        Type: main
  BibRelationships:
    HasContributorRelationships:
      – PersonEntity:
          Name:
            NameFull: Janßen, Holger
      – PersonEntity:
          Name:
            NameFull: Ehmcke, Luisa
      – PersonEntity:
          Name:
            NameFull: Satola, Barbara
      – PersonEntity:
          Name:
            NameFull: Kroener, Michael
      – PersonEntity:
          Name:
            NameFull: Dyck, Alexander
      – PersonEntity:
          Name:
            NameFull: Vehse, Martin
      – PersonEntity:
          Name:
            NameFull: Wark, Michael
      – PersonEntity:
          Name:
            NameFull: Agert, Carsten
    IsPartOfRelationships:
      – BibEntity:
          Dates:
            – D: 22
              M: 03
              Text: Mar2024
              Type: published
              Y: 2024
          Identifiers:
            – Type: issn-print
              Value: 03603199
          Numbering:
            – Type: volume
              Value: 60
          Titles:
            – TitleFull: International Journal of Hydrogen Energy
              Type: main
ResultId 1