Chemical Degradation of the Ternary Al2O3–YAG–ZrO2 Eutectic Ceramic by Molten CMAS.

Saved in:
Bibliographic Details
Title: Chemical Degradation of the Ternary Al2O3–YAG–ZrO2 Eutectic Ceramic by Molten CMAS.
Authors: Portebois, L.1 (AUTHOR) leo.portebois@univ-lorraine.fr, Mathieu, S.1 (AUTHOR), Vilasi, M.1 (AUTHOR), Berthod, P.1 (AUTHOR), Panteix, P-J.1 (AUTHOR), Podgorski, M.2 (AUTHOR)
Source: High Temperature Corrosion of Materials. Oct2024, Vol. 101 Issue 5, p1117-1128. 12p.
Subjects: Heat resistant materials, Eutectic reactions, Chemical decomposition, Turbine blades, Airplane motors, Eutectics
Abstract: Regarding potential high temperature applications of materials based on the ternary Al2O3-YAG-ZrO2 (AYZ) eutectic system for turbine blades, their environmental behaviour has to be evaluated in near-service conditions. CMAS attack is one of the phenomena limiting lifetime of ceramic E/TBC coatings for aircraft engines. The present study reports an assessment of the reactivity of AYZ eutectic material facing with two molten CMAS. The effect of test duration (up to 500 h), CMAS composition (with or without Fe2O3), microstructure (interlamellar distance), temperature (1250 and 1350 °C) as well as thermal cycling resistance were investigated. Results evidenced that the interaction of CMAS with AYZ eutectic ceramic was limited regardless of the microstructure. No infiltration of molten CMAS within the eutectic ceramic nor mechanical rupture between CMAS and AYZ was observed. The dissolution of AYZ leads to the rapid formation of anorthite with the CMAS components that hinders further reactions. The inward growth of MgAl2O4 spinel in place of the Al2O3 network occurs in accordance with the thermodynamic available data and without any effect on AYZ integrity. [ABSTRACT FROM AUTHOR]
Copyright of High Temperature Corrosion of Materials is the property of Springer Nature and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Description
Abstract:Regarding potential high temperature applications of materials based on the ternary Al2O3-YAG-ZrO2 (AYZ) eutectic system for turbine blades, their environmental behaviour has to be evaluated in near-service conditions. CMAS attack is one of the phenomena limiting lifetime of ceramic E/TBC coatings for aircraft engines. The present study reports an assessment of the reactivity of AYZ eutectic material facing with two molten CMAS. The effect of test duration (up to 500 h), CMAS composition (with or without Fe2O3), microstructure (interlamellar distance), temperature (1250 and 1350 °C) as well as thermal cycling resistance were investigated. Results evidenced that the interaction of CMAS with AYZ eutectic ceramic was limited regardless of the microstructure. No infiltration of molten CMAS within the eutectic ceramic nor mechanical rupture between CMAS and AYZ was observed. The dissolution of AYZ leads to the rapid formation of anorthite with the CMAS components that hinders further reactions. The inward growth of MgAl2O4 spinel in place of the Al2O3 network occurs in accordance with the thermodynamic available data and without any effect on AYZ integrity. [ABSTRACT FROM AUTHOR]