Experimental determination of probabilistic edge-delamination strength of a graphite–fiber/epoxy composite

Saved in:
Bibliographic Details
Title: Experimental determination of probabilistic edge-delamination strength of a graphite–fiber/epoxy composite
Authors: Wu, Xiang-Fa xfwu@unlserve.unl.edu, Dzenis, Yuris A.1
Source: Composite Structures. Aug2005, Vol. 70 Issue 1, p100-108. 9p.
Subjects: Graphite, Carbon, Native element minerals, Electron microscopes
Abstract: Abstract: Probabilistic edge-delamination strength of a thermosetting polymer composite was studied experimentally in this work. During the procedure, by means of edge-delamination tensile test, the graphite–fiber/epoxy laminate made of unidirectional Toray P7051S-20Q-1000 prepregs with an optimized lay-up of [122/–122/02]S was used for examining its probabilistic distributions of the edge-delamination onset stress and the ultimate tensile strength. Acoustic emission (AE) equipment and optical microscope were utilized to capture the edge-delamination initiation and characterize the failure modes during delaminating. Fractographical analysis based on scanning electron microscope (SEM) was conducted for the characterization of the microscopic failure mechanisms of the composite laminate during edge delaminating. Probabilistic models were introduced for data reduction. Test results show that the edge-delamination onset stress and the ultimate tensile strength of the laminate tested satisfy two two-parameter Weibull distributions very well. AE signals show the main failure mode during edge delaminating is interlaminar shear failure, corresponding to that predicted by numerical simulation and confirmed by SEM fractographical results in this study. [Copyright &y& Elsevier]
Copyright of Composite Structures is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Description
Abstract:Abstract: Probabilistic edge-delamination strength of a thermosetting polymer composite was studied experimentally in this work. During the procedure, by means of edge-delamination tensile test, the graphite–fiber/epoxy laminate made of unidirectional Toray P7051S-20Q-1000 prepregs with an optimized lay-up of [122/–122/02]S was used for examining its probabilistic distributions of the edge-delamination onset stress and the ultimate tensile strength. Acoustic emission (AE) equipment and optical microscope were utilized to capture the edge-delamination initiation and characterize the failure modes during delaminating. Fractographical analysis based on scanning electron microscope (SEM) was conducted for the characterization of the microscopic failure mechanisms of the composite laminate during edge delaminating. Probabilistic models were introduced for data reduction. Test results show that the edge-delamination onset stress and the ultimate tensile strength of the laminate tested satisfy two two-parameter Weibull distributions very well. AE signals show the main failure mode during edge delaminating is interlaminar shear failure, corresponding to that predicted by numerical simulation and confirmed by SEM fractographical results in this study. [Copyright &y& Elsevier]
ISSN:02638223
DOI:10.1016/j.compstruct.2004.08.016