Feasibility study of twin roll casting process for magnesium alloys

Saved in:
Bibliographic Details
Title: Feasibility study of twin roll casting process for magnesium alloys
Authors: Watari, H.1 watari@oyama-ct.ac.jp, Haga, T.2, Koga, N.3, Davey, K.4
Source: Journal of Materials Processing Technology. Sep2007, Vol. 192-193, p300-305. 6p.
Subjects: Chemical molding, Chemical engineering, Powder injection molding, Injection molding of ceramics
Abstract: Abstract: This paper is concerned with the development of a strip casting technology for manufacturing magnesium alloy sheets. The aim of the work is to establish a manufacturing process and technology to facilitate the economical manufacture of high-quality magnesium alloy sheets. Magnesium alloy AZ31, AZ61, AM60 and AZ91 were used to investigate the appropriate manufacturing conditions for use in twin roll strip casting. Temperatures of the molten materials and roll speeds were varied to find the appropriate manufacturing conditions. The effects of manufacturing conditions on possible forming were clarified in terms of roll speeds and roll gaps between upper and lower rolls. In addition, microscopic observation of the microstructure of the finished casting was performed. It was clarified that a magnesium sheet of 2.5–4.5mm thickness could be produced at a speed of 20m/min by a horizontal copper roll caster. Mill stiffness and a method of predicting the cast sheet''s thickness were investigated to determine the appropriate manufacturing conditions. It was also found that the cast magnesium sheet of AZ31, AZ61, AM60 and AZ91 manufactured by roll strip casting could be used for plastic forming if the appropriate magnesium sheets were produced after the roll casting process. By a warm deep-drawing test, it also demonstrated that a limiting drawing ratio of 2.4 was possible in the case of AZ91 sheet that was difficult to be manufactured by conventional extrusion process or DC casting and hot-rolling process for magesium alloy sheets with high aluminium contents. [Copyright &y& Elsevier]
Copyright of Journal of Materials Processing Technology is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Description
Abstract:Abstract: This paper is concerned with the development of a strip casting technology for manufacturing magnesium alloy sheets. The aim of the work is to establish a manufacturing process and technology to facilitate the economical manufacture of high-quality magnesium alloy sheets. Magnesium alloy AZ31, AZ61, AM60 and AZ91 were used to investigate the appropriate manufacturing conditions for use in twin roll strip casting. Temperatures of the molten materials and roll speeds were varied to find the appropriate manufacturing conditions. The effects of manufacturing conditions on possible forming were clarified in terms of roll speeds and roll gaps between upper and lower rolls. In addition, microscopic observation of the microstructure of the finished casting was performed. It was clarified that a magnesium sheet of 2.5–4.5mm thickness could be produced at a speed of 20m/min by a horizontal copper roll caster. Mill stiffness and a method of predicting the cast sheet''s thickness were investigated to determine the appropriate manufacturing conditions. It was also found that the cast magnesium sheet of AZ31, AZ61, AM60 and AZ91 manufactured by roll strip casting could be used for plastic forming if the appropriate magnesium sheets were produced after the roll casting process. By a warm deep-drawing test, it also demonstrated that a limiting drawing ratio of 2.4 was possible in the case of AZ91 sheet that was difficult to be manufactured by conventional extrusion process or DC casting and hot-rolling process for magesium alloy sheets with high aluminium contents. [Copyright &y& Elsevier]