The effect of neutron irradiation damage on the properties of grade NBG-10 graphite
Saved in:
| Title: | The effect of neutron irradiation damage on the properties of grade NBG-10 graphite |
|---|---|
| Authors: | Burchell, Timothy D. burchelltd@ornl.gov, Snead, Lance L.1 |
| Source: | Journal of Nuclear Materials. Sep2007, Vol. 371 Issue 1-3, p18-27. 10p. |
| Subjects: | Materials, Nuclear science, Physical sciences, Nuclear physics |
| Abstract: | Abstract: Nuclear block graphite-10 (NBG-10) is a medium-grain, near-isotropic graphite manufactured by SGL Carbon Company at their plant in Chedde, France. NBG-10 graphite was developed as a candidate core structural material for the pebble bed modular reactor (PBMR) currently being designed in South Africa, and for prismatic reactor concepts being developed in the USA and Europe. NBG-10 is one of several graphites included in the US-DOE Very High Temperature Reactor (VHTR) program. Thirty-six NBG-10 graphite flexure bars have been successfully irradiated in a series of 18 HFIR PTT capsules at ORNL. The capsule irradiation temperatures were 294±25, 360±25 and 691±25°C. The peak doses attained were 4.93, 6.67, and 6.69×1025 n/m2 [E >0.1MeV] at ∼294, ∼360, and ∼691°C, respectively. The high temperature irradiation volume and dimensional change behavior, and flexure strength and elastic modulus changes of NBG-10 were similar to other extruded, near-isotropic grades, such as H-451, which has been irradiated previously at ORNL. The low temperature (∼294°C) irradiation volume and dimensional change behavior was also as expected for extruded graphites, i.e., exhibiting low dose swelling prior to shrinkage. This behavior was attributed to the relaxation of internal stress arising from the graphite manufacturing process and specimen machining. While the data reported here do not represent a complete database for NBG-10 graphite, they give a measure of confidence that the current generation of nuclear graphites will behave in a familiar and well understood manner. [Copyright &y& Elsevier] |
| Copyright of Journal of Nuclear Materials is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| Database: | Engineering Source |