Structural, optical and electrical properties of post annealed Mg doped ZnO films for optoelectronics applications.

Saved in:

Bibliographic Details
Title:	Structural, optical and electrical properties of post annealed Mg doped ZnO films for optoelectronics applications.
Authors:	Sonawane, B.¹, Bhole, M.¹, Patil, D.¹ patildsp@rediffmail.com
Source:	Optical & Quantum Electronics. Jan2009, Vol. 41 Issue 1, p17-26. 10p. 1 Diagram, 1 Chart, 6 Graphs.
Subjects:	Electron microscopy, Semiconductor characterization, Optical properties, Spectroradiometer, Particles (Nuclear physics), Spectrophotometers, Scanning electron microscopy
Abstract:	Mg xZn1- xO films with 0.15 mole composition of Magnesium were successfully deposited by the spin coating sol–gel method. Zinc acetate dihydrate and Magnesium acetate were used as starting precursors to prepare the solution in ethanol solvent. The MgZnO films were deposited on microscopic glass substrates and post annealed at three different temperatures. X-ray Diffractometer (XRD), Scanning Electron Microscopy (SEM) and UV–VIS Spectrophotometer were used to characterize the deposited films for studying structural and optical properties. Energy dispersive analysis by X-ray (EDAX) was used to determine incorporation of Mg content in ZnO films. XRD spectrum reveals that, the deposited Mg doped ZnO films were polycrystalline in nature. The intensity of c-axis in the XRD spectrum goes on decreasing as Mg composition slightly increasing corresponding to increase in annealing temperature. EDAX spectra clearly showed the incorporation of Mg into the ZnO films. Semiconductor characterization system was used for the I–V characterization of MgZnO films. I–V characteristics show decrease in current as increase in the biased voltage. Optical band gap of MgZnO films was found to be increased from 3.2 to 3.38 eV as estimated from the absorption coefficients. [ABSTRACT FROM AUTHOR]
	Copyright of Optical & Quantum Electronics is the property of Springer Nature and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database:	Engineering Source

Description
Abstract:	Mg xZn1- xO films with 0.15 mole composition of Magnesium were successfully deposited by the spin coating sol–gel method. Zinc acetate dihydrate and Magnesium acetate were used as starting precursors to prepare the solution in ethanol solvent. The MgZnO films were deposited on microscopic glass substrates and post annealed at three different temperatures. X-ray Diffractometer (XRD), Scanning Electron Microscopy (SEM) and UV–VIS Spectrophotometer were used to characterize the deposited films for studying structural and optical properties. Energy dispersive analysis by X-ray (EDAX) was used to determine incorporation of Mg content in ZnO films. XRD spectrum reveals that, the deposited Mg doped ZnO films were polycrystalline in nature. The intensity of c-axis in the XRD spectrum goes on decreasing as Mg composition slightly increasing corresponding to increase in annealing temperature. EDAX spectra clearly showed the incorporation of Mg into the ZnO films. Semiconductor characterization system was used for the I–V characterization of MgZnO films. I–V characteristics show decrease in current as increase in the biased voltage. Optical band gap of MgZnO films was found to be increased from 3.2 to 3.38 eV as estimated from the absorption coefficients. [ABSTRACT FROM AUTHOR]
ISSN:	03068919
DOI:	10.1007/s11082-009-9317-y