Unveiling the Microstructural Features during Compression of a High-Modulus Mg-15Gd-8Y-6Al-0.3Mn Alloy Reinforced by a Large Volume of Al 2 RE Phases.
Saved in:
| Title: | Unveiling the Microstructural Features during Compression of a High-Modulus Mg-15Gd-8Y-6Al-0.3Mn Alloy Reinforced by a Large Volume of Al 2 RE Phases. |
|---|---|
| Authors: | Feng, Xuhui1 (AUTHOR) lixuejian@hit.edu.cn, Wang, Xiaojun1 (AUTHOR) xjwang@hit.edu.cn, Xu, Chao2 (AUTHOR) xjwang@hit.edu.cn, Shi, Hailong1 (AUTHOR), Li, Xuejian1 (AUTHOR), Hu, Xiaoshi1 (AUTHOR), Lu, Zhen1 (AUTHOR), Fan, Guohua3 (AUTHOR) |
| Source: | Materials (1996-1944). Oct2024, Vol. 17 Issue 19, p4784. 19p. |
| Subjects: | Isothermal compression, Strain rate, Elastic modulus, Recrystallization (Metallurgy), Microstructure |
| Abstract: | Magnesium alloys with a high volume fraction of secondary phases exhibit inferior formability. Therefore, investigating their thermal deformation characteristics is critical for optimizing thermal processing techniques. In this work, isothermal compression experiments were performed on a Mg-15Gd-8Y-6Al-0.3Mn alloy with an elastic modulus of 51.3 GPa with a substantial volume of aluminum-rare earth (Al2RE) phases. The rheological behavior and microstructural evolution of the material were systematically investigated at varying temperatures (350–500 °C) and strain rates (0.001–1.000 s−1). The calculated thermal processing diagram indicates that the unstable region gradually enlarges with increased strain, and all unstable regions appear within the high-strain-rate, low-temperature domain. The ideal thermal processing range of the alloy is 350–500 °C at strain rates ranging from 0.001 to 0.016 s−1. Particle-stimulated nucleation and discontinuous dynamic recrystallization are both verified to be responsible for the recrystallized microstructure of the alloy. The recrystallized grains exhibit a relatively random crystallographic orientation. As recrystallization proceeds, the texture gradually transitions from a typical [0001] texture in the compression direction to a random texture accompanied by decreased texture intensity. This work sheds new light on the thermo-mechanical processing of high-modulus Mg alloys, which could help design suitable processing techniques for related materials. [ABSTRACT FROM AUTHOR] |
| Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| Database: | Engineering Source |
|
Full text is not displayed to guests.
Login for full access.
|
|
| Abstract: | Magnesium alloys with a high volume fraction of secondary phases exhibit inferior formability. Therefore, investigating their thermal deformation characteristics is critical for optimizing thermal processing techniques. In this work, isothermal compression experiments were performed on a Mg-15Gd-8Y-6Al-0.3Mn alloy with an elastic modulus of 51.3 GPa with a substantial volume of aluminum-rare earth (Al2RE) phases. The rheological behavior and microstructural evolution of the material were systematically investigated at varying temperatures (350–500 °C) and strain rates (0.001–1.000 s−1). The calculated thermal processing diagram indicates that the unstable region gradually enlarges with increased strain, and all unstable regions appear within the high-strain-rate, low-temperature domain. The ideal thermal processing range of the alloy is 350–500 °C at strain rates ranging from 0.001 to 0.016 s−1. Particle-stimulated nucleation and discontinuous dynamic recrystallization are both verified to be responsible for the recrystallized microstructure of the alloy. The recrystallized grains exhibit a relatively random crystallographic orientation. As recrystallization proceeds, the texture gradually transitions from a typical [0001] texture in the compression direction to a random texture accompanied by decreased texture intensity. This work sheds new light on the thermo-mechanical processing of high-modulus Mg alloys, which could help design suitable processing techniques for related materials. [ABSTRACT FROM AUTHOR] |
|---|---|