Fabrication and characterization of biodegradable Zn-Ni spinel ferrite/ β-TCP composite ceramics exhibiting enhanced cell colonization.
Saved in:
| Title: | Fabrication and characterization of biodegradable Zn-Ni spinel ferrite/ β-TCP composite ceramics exhibiting enhanced cell colonization. |
|---|---|
| Authors: | Pankaew, Piyapong1 (AUTHOR), Nawarat, Poomirat1 (AUTHOR), Chokboribal, Jaroenporn2 (AUTHOR) chokboribal.j@gmail.com |
| Source: | Journal of Materials Science: Materials in Medicine. 1/29/2026, Vol. 37 Issue 1, p1-17. 17p. |
| Subjects: | Tissue engineering, Cytocompatibility, Ceramics, Nickel ferrite, Calcium phosphate, Bone surgery, Cell adhesion, Biodegradable products |
| Abstract: | Via a solid-state reaction route, magnetic composites of chicken eggshell-derived β-tricalcium phosphate (β-TCP, referred to as TCP in the composite system) and zinc-nickel spinel ferrite (ZNF; ZnxNi1‒xFe2O4, x = 0.2, 0.4, 0.6, or 0.8) were successfully fabricated. Discs were prepared by uniaxial pressing of milled ZNF/TCP powders and sintered at 1200 °C. Cytocompatibility of all composites was confirmed by SEM observations of human osteoblasts (h-OBs) and MTT assays. At 4-wt% ZNF addition, the composites containing Zn0.8Ni0.2Fe2O4 (Z8NF) exhibited the greatest extent of early cell spreading and were selected for further investigation. For Z8NF/TCP composites containing 4–12 wt% Z8NF, the 8–12 wt% samples demonstrated the highest levels of cell colonization, while MTT assays suggested non-cytotoxic behavior, with cell viabilities comparable to β-TCP. High-temperature sintering induced partial transformation of β-TCP to β-calcium pyrophosphate (β-CPP), as evidenced by XRD and Rietveld refinement. Increasing Z8NF content promoted β-CPP formation and increased composite porosity, whereas densification and Vickers hardness decreased accordingly. Rietveld refinement further indicated that the detectable crystalline Z8NF phase persisted as a minor yet stable secondary phase (< 2 wt%) and did not participate in Ca–P lattice substitution. For the 8–12 wt% composites, saturation magnetization decreased with increasing Z8NF because of higher porosity and dilution by the non-magnetic β-TCP/β-CPP matrix, while coercivity increased owing to enhanced effective magnetic anisotropy in the more porous microstructure. Overall, the Z8NF/TCP composites combined biodegradability, bioactivity, and tunable soft-magnetic properties, suggesting their potential for bone repair and bone tissue engineering applications. [ABSTRACT FROM AUTHOR] |
| Copyright of Journal of Materials Science: Materials in Medicine is the property of Springer Nature and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| Database: | Engineering Source |
|
Full text is not displayed to guests.
Login for full access.
|
|
| Abstract: | Via a solid-state reaction route, magnetic composites of chicken eggshell-derived β-tricalcium phosphate (β-TCP, referred to as TCP in the composite system) and zinc-nickel spinel ferrite (ZNF; ZnxNi1‒xFe2O4, x = 0.2, 0.4, 0.6, or 0.8) were successfully fabricated. Discs were prepared by uniaxial pressing of milled ZNF/TCP powders and sintered at 1200 °C. Cytocompatibility of all composites was confirmed by SEM observations of human osteoblasts (h-OBs) and MTT assays. At 4-wt% ZNF addition, the composites containing Zn0.8Ni0.2Fe2O4 (Z8NF) exhibited the greatest extent of early cell spreading and were selected for further investigation. For Z8NF/TCP composites containing 4–12 wt% Z8NF, the 8–12 wt% samples demonstrated the highest levels of cell colonization, while MTT assays suggested non-cytotoxic behavior, with cell viabilities comparable to β-TCP. High-temperature sintering induced partial transformation of β-TCP to β-calcium pyrophosphate (β-CPP), as evidenced by XRD and Rietveld refinement. Increasing Z8NF content promoted β-CPP formation and increased composite porosity, whereas densification and Vickers hardness decreased accordingly. Rietveld refinement further indicated that the detectable crystalline Z8NF phase persisted as a minor yet stable secondary phase (< 2 wt%) and did not participate in Ca–P lattice substitution. For the 8–12 wt% composites, saturation magnetization decreased with increasing Z8NF because of higher porosity and dilution by the non-magnetic β-TCP/β-CPP matrix, while coercivity increased owing to enhanced effective magnetic anisotropy in the more porous microstructure. Overall, the Z8NF/TCP composites combined biodegradability, bioactivity, and tunable soft-magnetic properties, suggesting their potential for bone repair and bone tissue engineering applications. [ABSTRACT FROM AUTHOR] |
|---|---|