Effect of the Physical and Chemical Characteristics of Polycarboxylate Ether Superplasticizers on the Spreading of Calcined Clays with Different Metakaolinite Contents Suspended in Synthetic Cement Pore Solution.
Saved in:
| Title: | Effect of the Physical and Chemical Characteristics of Polycarboxylate Ether Superplasticizers on the Spreading of Calcined Clays with Different Metakaolinite Contents Suspended in Synthetic Cement Pore Solution. |
|---|---|
| Authors: | Cruz, Suylan Matias1 (AUTHOR) matias.civileng@gmail.com, Lima, Ítalo Ribeiro Gonçalves1,2 (AUTHOR), Serafim, Maria José Souza1 (AUTHOR), Tobón, Jorge Iván2 (AUTHOR), Rêgo, João Henrique Silva1 (AUTHOR) |
| Source: | Materials (1996-1944). Apr2026, Vol. 19 Issue 8, p1516. 27p. |
| Subjects: | Polymer structure, Clay, Dispersion (Chemistry) |
| Abstract: | This study investigates the influence of the physical and chemical characteristics of three polycarboxylate ether (PCE) superplasticizers—differing in main-chain length, side-chain density, and dispersing-to-stabilizing polymer ratio (75:25, 50:50, and 25:75)—on the dispersion of calcined clays with varying metakaolinite contents (30.04–74.91 wt%) in synthetic cement pore solution (SCPS). Clays were characterized by XRF, XRD, TGA, FTIR, BET, Blaine fineness, and particle size distribution; PCEs were characterized by FTIR, 1H NMR, GPC, and zeta potential. Dispersion was assessed via mini-slump tests for water demand, PCE dosage to achieve 260 ± 5 mm spread, and slump retention over 120 min, quantified by a normalized spread retention index (SR120). Results revealed that clays with a higher metakaolinite content (58.45–74.91 wt%) and Blaine fineness (up to 13.116 m2/g) required two times higher PCE dosages and exhibited greater water demand due to enhanced surface reactivity and Ca2+/carboxylate affinity. Slump retention depended on PCE–clay compatibility: at a low metakaolinite content (30.04 wt%), all PCEs yielded SR120 ≈ 1; at higher contents, dispersing-rich PCEs (e.g., 75:25 ratio) sustained superior retention (SR120 > 1 in intermediate cases), while stabilizing-rich variants showed rapid loss. Zeta potential values remained close to zero due to the high ionic strength of the SCPS, indicating that electrostatic interactions play only a secondary role in the dispersion process, while steric effects govern the performance of the investigated PCEs. Overall, optimal PCE selection requires matching polymer architecture to clay reactivity for effective dispersion and fluidity retention in sustainable calcined clay systems. [ABSTRACT FROM AUTHOR] |
| Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| Database: | Engineering Source |
|
Full text is not displayed to guests.
Login for full access.
|
|
| Abstract: | This study investigates the influence of the physical and chemical characteristics of three polycarboxylate ether (PCE) superplasticizers—differing in main-chain length, side-chain density, and dispersing-to-stabilizing polymer ratio (75:25, 50:50, and 25:75)—on the dispersion of calcined clays with varying metakaolinite contents (30.04–74.91 wt%) in synthetic cement pore solution (SCPS). Clays were characterized by XRF, XRD, TGA, FTIR, BET, Blaine fineness, and particle size distribution; PCEs were characterized by FTIR, 1H NMR, GPC, and zeta potential. Dispersion was assessed via mini-slump tests for water demand, PCE dosage to achieve 260 ± 5 mm spread, and slump retention over 120 min, quantified by a normalized spread retention index (SR120). Results revealed that clays with a higher metakaolinite content (58.45–74.91 wt%) and Blaine fineness (up to 13.116 m2/g) required two times higher PCE dosages and exhibited greater water demand due to enhanced surface reactivity and Ca2+/carboxylate affinity. Slump retention depended on PCE–clay compatibility: at a low metakaolinite content (30.04 wt%), all PCEs yielded SR120 ≈ 1; at higher contents, dispersing-rich PCEs (e.g., 75:25 ratio) sustained superior retention (SR120 > 1 in intermediate cases), while stabilizing-rich variants showed rapid loss. Zeta potential values remained close to zero due to the high ionic strength of the SCPS, indicating that electrostatic interactions play only a secondary role in the dispersion process, while steric effects govern the performance of the investigated PCEs. Overall, optimal PCE selection requires matching polymer architecture to clay reactivity for effective dispersion and fluidity retention in sustainable calcined clay systems. [ABSTRACT FROM AUTHOR] |
|---|---|
| ISSN: | 19961944 |
| DOI: | 10.3390/ma19081516 |