Effect of SiC Content on Microstructure and Mechanical Properties of CoCrFeNi High-Entropy Alloy Composites.
Saved in:
| Title: | Effect of SiC Content on Microstructure and Mechanical Properties of CoCrFeNi High-Entropy Alloy Composites. |
|---|---|
| Authors: | Li, Ning1,2,3 (AUTHOR), Hu, Xinlong1,2 (AUTHOR), Wu, Chengbo1,3 (AUTHOR), Jiang, Mengyuan1 (AUTHOR), Li, Huiying1,2 (AUTHOR), Zhang, Jinlong1,3 (AUTHOR), Dong, Fuyuan1,2,3 (AUTHOR) fydong@alum.imr.ac.cn |
| Source: | Materials (1996-1944). Jun2026, Vol. 19 Issue 12, p2501. 14p. |
| Subjects: | Silicon carbide, Microstructure, Wear resistance, High-entropy alloys, Sintering, Carbides, Mechanical behavior of materials, Grain refinement |
| Abstract: | In this work, to address the limitation of low strength and hardness of single-phase CoCrFeNi high-entropy alloy, SiC particles were introduced as a reinforcing phase to prepare CoCrFeNi matrix composites with SiC contents of 0 wt%, 1 wt%, 2.5 wt% and 5 wt% via spark plasma sintering (SPS). It was preliminarily predicted that SiC particles would be uniformly distributed along grain boundaries of the CoCrFeNi matrix. During sintering, partial SiC decomposes at high-temperature, high-activity interfaces, regulating carbide precipitation and phase structural evolution, while residual undecomposed SiC remains at grain boundaries to pin boundaries and refine grains, thereby synergistically enhancing mechanical properties and wear resistance. Microstructural characterization reveals that all samples maintain a face-centered cubic (FCC) solid-solution matrix, and samples with non-zero SiC addition contain Cr7C3 carbides, which are mostly distributed at grain boundaries. With the increase in SiC content, mechanical performance is remarkably improved compared with the unreinforced CoCrFeNi matrix: the hardness rises from 198.8 HV to 321.7 HV, the yield strength is greatly enhanced from 242.5 MPa to 673.4 MPa, and the tensile strength increases from 557.9 MPa to 755.7 MPa. The improved yield strength originates synergistically from grain refinement, solid-solution strengthening, grain-boundary strengthening and dislocation strengthening. By clarifying the influence of microstructural defects on critical shear stress (τ0) and normal fracture stress (σ0), the intrinsic mechanism governing tensile mechanical performance and ductile–brittle fracture transition was revealed. This optimized CoCrFeNi/SiC composite exhibits excellent strength–hardness comprehensive performance, showing promising application potential for high-load, wear-resistant and structural service components under severe tribological and pressure conditions. [ABSTRACT FROM AUTHOR] |
| Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) | |
| Database: | Engineering Source |
|
Full text is not displayed to guests.
Login for full access.
|
|
| Abstract: | In this work, to address the limitation of low strength and hardness of single-phase CoCrFeNi high-entropy alloy, SiC particles were introduced as a reinforcing phase to prepare CoCrFeNi matrix composites with SiC contents of 0 wt%, 1 wt%, 2.5 wt% and 5 wt% via spark plasma sintering (SPS). It was preliminarily predicted that SiC particles would be uniformly distributed along grain boundaries of the CoCrFeNi matrix. During sintering, partial SiC decomposes at high-temperature, high-activity interfaces, regulating carbide precipitation and phase structural evolution, while residual undecomposed SiC remains at grain boundaries to pin boundaries and refine grains, thereby synergistically enhancing mechanical properties and wear resistance. Microstructural characterization reveals that all samples maintain a face-centered cubic (FCC) solid-solution matrix, and samples with non-zero SiC addition contain Cr7C3 carbides, which are mostly distributed at grain boundaries. With the increase in SiC content, mechanical performance is remarkably improved compared with the unreinforced CoCrFeNi matrix: the hardness rises from 198.8 HV to 321.7 HV, the yield strength is greatly enhanced from 242.5 MPa to 673.4 MPa, and the tensile strength increases from 557.9 MPa to 755.7 MPa. The improved yield strength originates synergistically from grain refinement, solid-solution strengthening, grain-boundary strengthening and dislocation strengthening. By clarifying the influence of microstructural defects on critical shear stress (τ0) and normal fracture stress (σ0), the intrinsic mechanism governing tensile mechanical performance and ductile–brittle fracture transition was revealed. This optimized CoCrFeNi/SiC composite exhibits excellent strength–hardness comprehensive performance, showing promising application potential for high-load, wear-resistant and structural service components under severe tribological and pressure conditions. [ABSTRACT FROM AUTHOR] |
|---|---|