Material damping in 6061-T6511 aluminium to assess fatigue damage.

Saved in:
Bibliographic Details
Title: Material damping in 6061-T6511 aluminium to assess fatigue damage.
Authors: COLAKOGLU, M.1, JERINA, K. L.2
Source: Fatigue & Fracture of Engineering Materials & Structures. Jan2003, Vol. 26 Issue 1, p79-84. 6p.
Subjects: Aluminum, Energy dissipation, Strength of materials
Abstract: ABSTRACT Studies in fatigue can be summarized into two stages, fatigue crack initiation and crack propagation. Fatigue damage may increase the risk of failure under cyclic load. Energy dissipation, termed damping, occurs in engineering metals and is a function of the cyclic loading history. Damping behaviour of materials has been estimated using many different experimental techniques, and parameters i.e. the loss factor vs. strain amplitude, frequency range, etc. However, micro-structural changes in the form of fatigue damage are also contributors to damping in engineering materials. In order to measure energy dissipation, a damping monitoring method has been used. Under a constant cyclic load up to the point of fatigue crack initiation, the effects of fatigue on damping factor were studied for 6061-T6511 aluminium alloy. In the experiments, the stress levels were below yield point, 50% and 70% of ultimate strength. Experimental results showed that the damping factor changes with the number of fatigue cycles. Percentage increase in damping energy was calculated using experimental data. [ABSTRACT FROM AUTHOR]
Copyright of Fatigue & Fracture of Engineering Materials & Structures is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Description
Abstract:ABSTRACT Studies in fatigue can be summarized into two stages, fatigue crack initiation and crack propagation. Fatigue damage may increase the risk of failure under cyclic load. Energy dissipation, termed damping, occurs in engineering metals and is a function of the cyclic loading history. Damping behaviour of materials has been estimated using many different experimental techniques, and parameters i.e. the loss factor vs. strain amplitude, frequency range, etc. However, micro-structural changes in the form of fatigue damage are also contributors to damping in engineering materials. In order to measure energy dissipation, a damping monitoring method has been used. Under a constant cyclic load up to the point of fatigue crack initiation, the effects of fatigue on damping factor were studied for 6061-T6511 aluminium alloy. In the experiments, the stress levels were below yield point, 50% and 70% of ultimate strength. Experimental results showed that the damping factor changes with the number of fatigue cycles. Percentage increase in damping energy was calculated using experimental data. [ABSTRACT FROM AUTHOR]
ISSN:8756758X
DOI:10.1046/j.1460-2695.2003.00603.x