Bonding of resin luting cements to dentine after casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) treatment.

Saved in:
Bibliographic Details
Title: Bonding of resin luting cements to dentine after casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) treatment.
Authors: Sattabanasuk, Vanthana1 vanthana.sat@mahidol.ac.th, Burrow, Michael F.2, Yasushi Shimada3, Junji Tagami3
Source: International Journal of Adhesion & Adhesives. Oct2014, Vol. 54, p93-99. 7p.
Subjects: Gums & resins, Dental cements, Phosphopeptides, Amorphous substances, Calcium phosphate, Dental bonding
Abstract: Objective: To determine whether the application of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) in the proprietary paste to dentine would affect the subsequent bonding of resin-based adhesive luting cements. Methods: Flat mid-coronal occlusal dentine surfaces of extracted human molars were prepared and randomly divided into three groups with different treatment periods of CPP-ACP-containing paste, Tooth MousseTM, i.e., no treatment; 5 min; or 5 days. Resin composite blocks were luted using either Variolink N, Panavia F2.0, Rely X U100, or Clearfil SA Luting, following the manufacturers' instructions. After storage in 100% relative humidity condition at 37 °C for 24 h, the bonded assemblies were sectioned perpendicular to the interface in x and y directions, obtaining stick-shaped specimens, to assess the adhesion using a microtensile bond strength test. Fractography and micromorphology of resin cement-dentine interface were examined under a SEM. Results: Dentine bond strengths of Variolink N and Rely X U100 appeared to be similar for all tested groups. Clearfil SA Luting showed a decrease of bond strength with a strong tendency for adhesive failure between resin cement and dentine following the CPP-ACP application. An increase of bond strength was observed for Panavia F2.0 bonded to CPP-ACP-treated dentine. Micromorphological evaluation revealed intimate interfacial contact and formation of pronounced resin tags for Variolink N and Panavia F2.0, regardless of CPP-ACP treatment. For the self-adhesive luting materials tested, no distinct interaction zone between the resin cements and dentine could be observed and fewer resin tags were formed. Voids at the interface were detected for Clearfil SA Luting bonded to dentine following the treatment of CPP-ACP for both application times. Conclusions: Prior application of the CPP-ACP-containing paste to dentine compromised the bonding effectiveness of self-adhesive resin cements. However, with separate pretreatment steps to the tooth surface, dentine adhesion of conventional resin cements seemed not to be negatively influenced by CPP-ACP application. [ABSTRACT FROM AUTHOR]
Copyright of International Journal of Adhesion & Adhesives is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Description
Abstract:Objective: To determine whether the application of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) in the proprietary paste to dentine would affect the subsequent bonding of resin-based adhesive luting cements. Methods: Flat mid-coronal occlusal dentine surfaces of extracted human molars were prepared and randomly divided into three groups with different treatment periods of CPP-ACP-containing paste, Tooth MousseTM, i.e., no treatment; 5 min; or 5 days. Resin composite blocks were luted using either Variolink N, Panavia F2.0, Rely X U100, or Clearfil SA Luting, following the manufacturers' instructions. After storage in 100% relative humidity condition at 37 °C for 24 h, the bonded assemblies were sectioned perpendicular to the interface in x and y directions, obtaining stick-shaped specimens, to assess the adhesion using a microtensile bond strength test. Fractography and micromorphology of resin cement-dentine interface were examined under a SEM. Results: Dentine bond strengths of Variolink N and Rely X U100 appeared to be similar for all tested groups. Clearfil SA Luting showed a decrease of bond strength with a strong tendency for adhesive failure between resin cement and dentine following the CPP-ACP application. An increase of bond strength was observed for Panavia F2.0 bonded to CPP-ACP-treated dentine. Micromorphological evaluation revealed intimate interfacial contact and formation of pronounced resin tags for Variolink N and Panavia F2.0, regardless of CPP-ACP treatment. For the self-adhesive luting materials tested, no distinct interaction zone between the resin cements and dentine could be observed and fewer resin tags were formed. Voids at the interface were detected for Clearfil SA Luting bonded to dentine following the treatment of CPP-ACP for both application times. Conclusions: Prior application of the CPP-ACP-containing paste to dentine compromised the bonding effectiveness of self-adhesive resin cements. However, with separate pretreatment steps to the tooth surface, dentine adhesion of conventional resin cements seemed not to be negatively influenced by CPP-ACP application. [ABSTRACT FROM AUTHOR]
ISSN:01437496
DOI:10.1016/j.ijadhadh.2014.05.008