Inorganic stabilisation methods for extruded earth masonry units.

Saved in:
Bibliographic Details
Title: Inorganic stabilisation methods for extruded earth masonry units.
Authors: Maskell, Daniel1 D.Maskell@bath.ac.uk, Heath, Andrew1, Walker, Pete1
Source: Construction & Building Materials. Nov2014, Vol. 71, p602-609. 8p.
Subjects: Inorganic chemistry, Extrusion process, Masonry, Environmental impact analysis, Durability, Earth construction
Abstract: Addressing the challenges of embodied environmental impact of materials has led to growing interest in the use of earth as a construction material. Adopting large-scale commercial methods of extruded brick production has potential to overcome many of the existing barriers of adoption. Without the firing the bricks will have a significantly lower embodied environmental impact and similar dimensions (just over 100 mm thick in the UK) to conventional masonry. However, the wider adoption of 100 mm thick unfired earth masonry is dependent on its suitability for use in structurally load-bearing applications. Currently the greatest barrier to earth masonry adoption is the durability of the material when subjected to high moisture contents. Accidental or intentional wetting of a 100 mm thick load bearing unfired earth wall could lead to disproportionate collapse unless the moisture resistance is improved. To overcome the concern of elevated moisture contents, a common approach is to chemically stabilise the soil using either cement or lime. While there has been research into the use of cement and lime for other forms of earth construction, their use for extruded earth bricks has not been investigated in depth. The source materials and inherent physical properties of extruded earth bricks are different to other forms of earthen construction. Therefore the suitability of cement and lime to stabilise soil for the purpose of extruded earth bricks requires investigation. This research demonstrates the improvement in 28 day compressive strength, with a range of cement or lime contents and three initial curing temperatures. Small scale bricks were tested in both the ambient environmental conditions and following 24 h of full submersion in water. Key factors, such as density and moisture content, are shown to be important for compressive strength development. The effect of stabilisation has been shown to be more important as a determinant for strength than density and moisture content alone. [ABSTRACT FROM AUTHOR]
Copyright of Construction & Building Materials is the property of Elsevier B.V. and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Engineering Source
Description
Abstract:Addressing the challenges of embodied environmental impact of materials has led to growing interest in the use of earth as a construction material. Adopting large-scale commercial methods of extruded brick production has potential to overcome many of the existing barriers of adoption. Without the firing the bricks will have a significantly lower embodied environmental impact and similar dimensions (just over 100 mm thick in the UK) to conventional masonry. However, the wider adoption of 100 mm thick unfired earth masonry is dependent on its suitability for use in structurally load-bearing applications. Currently the greatest barrier to earth masonry adoption is the durability of the material when subjected to high moisture contents. Accidental or intentional wetting of a 100 mm thick load bearing unfired earth wall could lead to disproportionate collapse unless the moisture resistance is improved. To overcome the concern of elevated moisture contents, a common approach is to chemically stabilise the soil using either cement or lime. While there has been research into the use of cement and lime for other forms of earth construction, their use for extruded earth bricks has not been investigated in depth. The source materials and inherent physical properties of extruded earth bricks are different to other forms of earthen construction. Therefore the suitability of cement and lime to stabilise soil for the purpose of extruded earth bricks requires investigation. This research demonstrates the improvement in 28 day compressive strength, with a range of cement or lime contents and three initial curing temperatures. Small scale bricks were tested in both the ambient environmental conditions and following 24 h of full submersion in water. Key factors, such as density and moisture content, are shown to be important for compressive strength development. The effect of stabilisation has been shown to be more important as a determinant for strength than density and moisture content alone. [ABSTRACT FROM AUTHOR]